PA66 AKV 35 000000德國朗盛Durethan 35%玻纖注塑尼龍66塑料（18024445500）

PA 66, 35% glass fibers, injection molding


ISO Shortname: ISO 1874-PA 66, MR, 14-120, GF35

Property Test Condition Unit Standard guide value
d.a.m. cond.
Rheological properties
Molding shrinkage, parallel 150x105x3; 300 °C / MT 80 °C; 400 bar % acc. ISO 2577 0.32　
Molding shrinkage, transverse 150x105x3; 300 °C / MT 80 °C; 400 bar % acc. ISO 2577 1.4　
Post- shrinkage, parallel 150x105x3; 120 °C; 4 h % acc. ISO 2577 0.03　
Post- shrinkage, transverse 150x105x3; 120 °C; 4 h % acc. ISO 2577 0.04　

Mechanical properties (23 °C/50 % r. h.)
C Tensile modulus 1 mm/min MPa ISO 527-1,-2 11200 7500
C Tensile Stress at break 5 mm/min MPa ISO 527-1,-2 200 135
C Tensile Strain at break 5 mm/min % ISO 527-1,-2 3.0 5.0
C Tensile creep modulus 1 h MPa ISO 899-1　7000
C Tensile creep modulus 1000 h MPa ISO 899-1　5800
C Charpy impact strength 23 °C kJ/m² ISO 179-1eU 90 95
C Charpy impact strength -30 °C kJ/m² ISO 179-1eU 75 75
C Charpy notched impact strength 23 °C kJ/m² ISO 179-1eA 15 20
C Charpy notched impact strength -30 °C kJ/m² ISO 179-1eA 10 10
Izod notched impact strength -30 °C kJ/m² ISO 180-1A < 10 < 10
Izod notched impact strength -40 °C kJ/m² ISO 180-1A < 10 < 10
Flexural modulus 2 mm/min MPa ISO 178-A 10000 7000
Flexural strength 2 mm/min MPa ISO 178-A 300 220
Flexural strain at flexural strength 2 mm/min % ISO 178-A 4.0 6.0
Flexural stress at 3.5 % strain 2 mm/min MPa ISO 178-A 280 170